2" Union PMV-11 Plane Iron
Union Thick PMV11 2 inch plane Irons. These Irons are designed to replace the Union Thick Irons on Union Mfg Co made planes including the X-Plane (But not Union Plane Co marked planes) . These irons are NOT compatible with vintage planes from Stanley, Record or other manufacturers. The Irons are Union thick at 0.125 inches.
All are lapped on the face side to a flatness tolerance of 0.0005" or better, with an average roughness (Ra) of 5 microinches (0.000005") or better.
PM-V11 is a powdered metal (PM) alloy. To form a PM alloy, constituent metals are melted and mixed together, then atomized, creating very small particles that cool and harden, forming a powder. This powder is screened to ensure consistent particle size and then heated under pressure to form a billet. The billet is then rolled to the required thickness, ready to process as a conventionally smelted steel would be. The PM process yields a steel with a very fine grain structure that is uniform throughout.
Made in Canada.
Union Thick PMV11 2 inch plane Irons. These Irons are designed to replace the Union Thick Irons on Union Mfg Co made planes including the X-Plane (But not Union Plane Co marked planes) . These irons are NOT compatible with vintage planes from Stanley, Record or other manufacturers. The Irons are Union thick at 0.125 inches.
All are lapped on the face side to a flatness tolerance of 0.0005" or better, with an average roughness (Ra) of 5 microinches (0.000005") or better.
PM-V11 is a powdered metal (PM) alloy. To form a PM alloy, constituent metals are melted and mixed together, then atomized, creating very small particles that cool and harden, forming a powder. This powder is screened to ensure consistent particle size and then heated under pressure to form a billet. The billet is then rolled to the required thickness, ready to process as a conventionally smelted steel would be. The PM process yields a steel with a very fine grain structure that is uniform throughout.
Made in Canada.
Union Thick PMV11 2 inch plane Irons. These Irons are designed to replace the Union Thick Irons on Union Mfg Co made planes including the X-Plane (But not Union Plane Co marked planes) . These irons are NOT compatible with vintage planes from Stanley, Record or other manufacturers. The Irons are Union thick at 0.125 inches.
All are lapped on the face side to a flatness tolerance of 0.0005" or better, with an average roughness (Ra) of 5 microinches (0.000005") or better.
PM-V11 is a powdered metal (PM) alloy. To form a PM alloy, constituent metals are melted and mixed together, then atomized, creating very small particles that cool and harden, forming a powder. This powder is screened to ensure consistent particle size and then heated under pressure to form a billet. The billet is then rolled to the required thickness, ready to process as a conventionally smelted steel would be. The PM process yields a steel with a very fine grain structure that is uniform throughout.
Made in Canada.
Union Tools are Exclusively available through Union and our retail partners
USA
Europe
Australia